EN 1.4849 Stainless Steel vs. Class 2 Tungsten
EN 1.4849 stainless steel belongs to the iron alloys classification, while class 2 tungsten belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.4849 stainless steel and the bottom bar is class 2 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 260 |
| Elongation at Break, % | 4.5 | |
| 5.7 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 100 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 120 |
| Thermal Conductivity, W/m-K | 12 | |
| 20 |
| Thermal Expansion, µm/m-K | 15 | |
| 4.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 7.1 | |
| 23 |
| Embodied Energy, MJ/kg | 100 | |
| 350 |
| Embodied Water, L/kg | 200 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 640 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 14 |
| Strength to Weight: Axial, points | 17 | |
| 16 |
| Strength to Weight: Bending, points | 17 | |
| 13 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 11 |
| Thermal Shock Resistance, points | 11 | |
| 52 |
Alloy Composition
| Carbon (C), % | 0.3 to 0.5 | |
| 0 |
| Chromium (Cr), % | 18 to 21 | |
| 0 |
| Iron (Fe), % | 32.6 to 43.5 | |
| 0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 36 to 39 | |
| 0 |
| Niobium (Nb), % | 1.2 to 1.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 1.0 to 2.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 0 | |
| 92.5 |
| Residuals, % | 0 | |
| 7.5 |