EN 1.4854 Stainless Steel vs. EN 1.8837 Steel

Both EN 1.4854 stainless steel and EN 1.8837 steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4854 stainless steel and the bottom bar is EN 1.8837 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
19
Fatigue Strength, MPa 310
340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 520
390
Tensile Strength: Ultimate (UTS), MPa 750
630
Tensile Strength: Yield (Proof), MPa 340
490

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1170
400
Melting Completion (Liquidus), °C 1370
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 11
49
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 34
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.7
1.6
Embodied Energy, MJ/kg 81
21
Embodied Water, L/kg 220
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
110
Resilience: Unit (Modulus of Resilience), kJ/m3 280
640
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
22
Strength to Weight: Bending, points 23
21
Thermal Diffusivity, mm2/s 2.9
13
Thermal Shock Resistance, points 18
18

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.040
Carbon (C), % 0.040 to 0.080
0 to 0.16
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 33.6 to 40.6
96.6 to 99.98
Manganese (Mn), % 0 to 2.0
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 34 to 36
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.12 to 0.2
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 1.2 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.1