EN 1.4864 Stainless Steel vs. CR023A Copper

EN 1.4864 stainless steel belongs to the iron alloys classification, while CR023A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is CR023A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 33
15
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 75
43
Tensile Strength: Ultimate (UTS), MPa 650
220
Tensile Strength: Yield (Proof), MPa 260
130

Thermal Properties

Latent Heat of Fusion, J/g 310
210
Maximum Temperature: Mechanical, °C 1100
200
Melting Completion (Liquidus), °C 1390
1090
Melting Onset (Solidus), °C 1340
1040
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 13
380
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
100
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
100

Otherwise Unclassified Properties

Base Metal Price, % relative 30
31
Density, g/cm3 8.0
9.0
Embodied Carbon, kg CO2/kg material 5.3
2.6
Embodied Energy, MJ/kg 75
41
Embodied Water, L/kg 180
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
29
Resilience: Unit (Modulus of Resilience), kJ/m3 170
76
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 23
6.8
Strength to Weight: Bending, points 21
9.0
Thermal Diffusivity, mm2/s 3.3
110
Thermal Shock Resistance, points 17
7.8

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 15 to 17
0
Copper (Cu), % 0
99.9 to 99.995
Iron (Fe), % 41.7 to 51
0
Lead (Pb), % 0
0 to 0.0050
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0.0050 to 0.013
Silicon (Si), % 1.0 to 2.0
0
Silver (Ag), % 0
0 to 0.015
Sulfur (S), % 0 to 0.015
0