EN 1.4864 Stainless Steel vs. SAE-AISI 1008 Steel

Both EN 1.4864 stainless steel and SAE-AISI 1008 steel are iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is SAE-AISI 1008 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
93 to 100
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 33
22 to 33
Fatigue Strength, MPa 200
150 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
73
Shear Strength, MPa 430
220 to 230
Tensile Strength: Ultimate (UTS), MPa 650
330 to 370
Tensile Strength: Yield (Proof), MPa 260
190 to 310

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1390
1470
Melting Onset (Solidus), °C 1340
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 13
62
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.3
1.4
Embodied Energy, MJ/kg 75
18
Embodied Water, L/kg 180
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
78 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 170
92 to 260
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
12 to 13
Strength to Weight: Bending, points 21
13 to 15
Thermal Diffusivity, mm2/s 3.3
17
Thermal Shock Resistance, points 17
10 to 12

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.1
Chromium (Cr), % 15 to 17
0
Iron (Fe), % 41.7 to 51
99.31 to 99.7
Manganese (Mn), % 0 to 2.0
0.3 to 0.5
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.0 to 2.0
0
Sulfur (S), % 0 to 0.015
0 to 0.050