EN 1.4864 Stainless Steel vs. SAE-AISI 1211 Steel

Both EN 1.4864 stainless steel and SAE-AISI 1211 steel are iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is SAE-AISI 1211 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 33
11 to 29
Fatigue Strength, MPa 200
200 to 280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
73
Shear Strength, MPa 430
280 to 350
Tensile Strength: Ultimate (UTS), MPa 650
430 to 580
Tensile Strength: Yield (Proof), MPa 260
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 30
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.3
1.4
Embodied Energy, MJ/kg 75
18
Embodied Water, L/kg 180
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
61 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
180 to 550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
15 to 21
Strength to Weight: Bending, points 21
16 to 20
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 17
14 to 18

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.13
Chromium (Cr), % 15 to 17
0
Iron (Fe), % 41.7 to 51
98.7 to 99.23
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0.070 to 0.12
Silicon (Si), % 1.0 to 2.0
0
Sulfur (S), % 0 to 0.015
0.1 to 0.15