EN 1.4864 Stainless Steel vs. SAE-AISI O6 Steel

Both EN 1.4864 stainless steel and SAE-AISI O6 steel are iron alloys. They have 48% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is SAE-AISI O6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
71
Tensile Strength: Ultimate (UTS), MPa 650
670 to 2070

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Melting Completion (Liquidus), °C 1390
1430
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 13
43
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.3
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.3
1.5
Embodied Energy, MJ/kg 75
21
Embodied Water, L/kg 180
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
24 to 74
Strength to Weight: Bending, points 21
22 to 47
Thermal Diffusivity, mm2/s 3.3
12
Thermal Shock Resistance, points 17
22 to 69

Alloy Composition

Carbon (C), % 0 to 0.15
1.3 to 1.6
Chromium (Cr), % 15 to 17
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 41.7 to 51
94.6 to 97.7
Manganese (Mn), % 0 to 2.0
0.3 to 1.1
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 33 to 37
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 1.0 to 2.0
0.55 to 1.5
Sulfur (S), % 0 to 0.015
0 to 0.030