EN 1.4864 Stainless Steel vs. C91700 Bronze

EN 1.4864 stainless steel belongs to the iron alloys classification, while C91700 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is C91700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
90
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 33
13
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 75
41
Tensile Strength: Ultimate (UTS), MPa 650
330
Tensile Strength: Yield (Proof), MPa 260
170

Thermal Properties

Latent Heat of Fusion, J/g 310
190
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1390
1020
Melting Onset (Solidus), °C 1340
850
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 13
71
Thermal Expansion, µm/m-K 14
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
10
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 30
36
Density, g/cm3 8.0
8.7
Embodied Carbon, kg CO2/kg material 5.3
3.9
Embodied Energy, MJ/kg 75
63
Embodied Water, L/kg 180
400

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
35
Resilience: Unit (Modulus of Resilience), kJ/m3 170
140
Stiffness to Weight: Axial, points 13
6.9
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 23
11
Strength to Weight: Bending, points 21
12
Thermal Diffusivity, mm2/s 3.3
22
Thermal Shock Resistance, points 17
12

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 15 to 17
0
Copper (Cu), % 0
84.2 to 87.5
Iron (Fe), % 41.7 to 51
0 to 0.2
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
1.2 to 2.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.3
Silicon (Si), % 1.0 to 2.0
0 to 0.0050
Sulfur (S), % 0 to 0.015
0 to 0.050
Tin (Sn), % 0
11.3 to 12.5
Zinc (Zn), % 0
0 to 0.25