EN 1.4864 stainless steel belongs to the iron alloys classification, while N06210 nickel belongs to the nickel alloys. They have 52% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is N06210 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 33
51
Fatigue Strength, MPa 200
320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
85
Shear Strength, MPa 430
560
Tensile Strength: Ultimate (UTS), MPa 650
780
Tensile Strength: Yield (Proof), MPa 260
350

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Maximum Temperature: Mechanical, °C 1100
980
Melting Completion (Liquidus), °C 1390
1570
Melting Onset (Solidus), °C 1340
1510
Specific Heat Capacity, J/kg-K 480
420
Thermal Expansion, µm/m-K 14
12

Otherwise Unclassified Properties

Base Metal Price, % relative 30
85
Density, g/cm3 8.0
9.0
Embodied Carbon, kg CO2/kg material 5.3
17
Embodied Energy, MJ/kg 75
250
Embodied Water, L/kg 180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
320
Resilience: Unit (Modulus of Resilience), kJ/m3 170
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 23
24
Strength to Weight: Bending, points 21
21
Thermal Shock Resistance, points 17
22

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.015
Chromium (Cr), % 15 to 17
18 to 20
Cobalt (Co), % 0
0 to 1.0
Iron (Fe), % 41.7 to 51
0 to 1.0
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 0
18 to 20
Nickel (Ni), % 33 to 37
54.8 to 62.5
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 1.0 to 2.0
0 to 0.080
Sulfur (S), % 0 to 0.015
0 to 0.020
Tantalum (Ta), % 0
1.5 to 2.2
Vanadium (V), % 0
0 to 0.35