EN 1.4869 Casting Alloy vs. C14200 Copper
EN 1.4869 casting alloy belongs to the nickel alloys classification, while C14200 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4869 casting alloy and the bottom bar is C14200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 120 |
| Elongation at Break, % | 5.7 | |
| 8.0 to 45 |
| Fatigue Strength, MPa | 130 | |
| 76 to 130 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 80 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 220 to 370 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 75 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 1200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1080 |
| Melting Onset (Solidus), °C | 1390 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 390 |
| Thermal Conductivity, W/m-K | 10 | |
| 190 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 31 |
| Density, g/cm3 | 8.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 110 | |
| 41 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 | |
| 29 to 83 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 | |
| 24 to 500 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 18 | |
| 6.8 to 11 |
| Strength to Weight: Bending, points | 17 | |
| 9.1 to 13 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 56 |
| Thermal Shock Resistance, points | 14 | |
| 7.9 to 13 |
Alloy Composition
| Arsenic (As), % | 0 | |
| 0.15 to 0.5 |
| Carbon (C), % | 0.45 to 0.55 | |
| 0 |
| Chromium (Cr), % | 24 to 26 | |
| 0 |
| Cobalt (Co), % | 14 to 16 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.4 to 99.835 |
| Iron (Fe), % | 11.4 to 23.6 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 33 to 37 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.015 to 0.040 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 4.0 to 6.0 | |
| 0 |