EN 1.4869 Casting Alloy vs. N08800 Stainless Steel
EN 1.4869 casting alloy belongs to the nickel alloys classification, while N08800 stainless steel belongs to the iron alloys. They have 72% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4869 casting alloy and the bottom bar is N08800 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 5.7 | |
| 4.5 to 34 |
| Fatigue Strength, MPa | 130 | |
| 150 to 390 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 500 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 190 to 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 1200 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1390 |
| Melting Onset (Solidus), °C | 1390 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 10 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 30 |
| Density, g/cm3 | 8.5 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 5.3 |
| Embodied Energy, MJ/kg | 110 | |
| 76 |
| Embodied Water, L/kg | 300 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 | |
| 42 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 | |
| 96 to 1740 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 18 to 35 |
| Strength to Weight: Bending, points | 17 | |
| 18 to 28 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 3.0 |
| Thermal Shock Resistance, points | 14 | |
| 13 to 25 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.15 to 0.6 |
| Carbon (C), % | 0.45 to 0.55 | |
| 0 to 0.1 |
| Chromium (Cr), % | 24 to 26 | |
| 19 to 23 |
| Cobalt (Co), % | 14 to 16 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 11.4 to 23.6 | |
| 39.5 to 50.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 33 to 37 | |
| 30 to 35 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |
| Tungsten (W), % | 4.0 to 6.0 | |
| 0 |