EN 1.4872 stainless steel belongs to the iron alloys classification, while C14500 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4872 stainless steel and the bottom bar is C14500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 28
12 to 50
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 79
43
Shear Strength, MPa 620
150 to 190
Tensile Strength: Ultimate (UTS), MPa 950
220 to 330
Tensile Strength: Yield (Proof), MPa 560
69 to 260

Thermal Properties

Latent Heat of Fusion, J/g 300
210
Maximum Temperature: Mechanical, °C 1150
200
Melting Completion (Liquidus), °C 1390
1080
Melting Onset (Solidus), °C 1340
1050
Specific Heat Capacity, J/kg-K 490
390
Thermal Conductivity, W/m-K 15
360
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
94
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
95

Otherwise Unclassified Properties

Base Metal Price, % relative 17
33
Density, g/cm3 7.6
8.9
Embodied Carbon, kg CO2/kg material 3.3
2.6
Embodied Energy, MJ/kg 47
42
Embodied Water, L/kg 180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
36 to 85
Resilience: Unit (Modulus of Resilience), kJ/m3 780
21 to 300
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 26
18
Strength to Weight: Axial, points 35
6.8 to 10
Strength to Weight: Bending, points 28
9.1 to 12
Thermal Diffusivity, mm2/s 3.9
100
Thermal Shock Resistance, points 21
8.0 to 12

Alloy Composition

Carbon (C), % 0.2 to 0.3
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
99.2 to 99.596
Iron (Fe), % 54.2 to 61.6
0
Manganese (Mn), % 8.0 to 10
0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.045
0.0040 to 0.012
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Tellurium (Te), % 0
0.4 to 0.7