EN 1.4874 Stainless Steel vs. EN 1.5501 Steel
Both EN 1.4874 stainless steel and EN 1.5501 steel are iron alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4874 stainless steel and the bottom bar is EN 1.5501 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 120 to 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 6.7 | |
| 12 to 17 |
| Fatigue Strength, MPa | 180 | |
| 180 to 270 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 390 to 510 |
| Tensile Strength: Yield (Proof), MPa | 360 | |
| 260 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1150 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 52 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 1.8 |
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 7.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 18 |
| Embodied Water, L/kg | 290 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 40 to 83 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 | |
| 190 to 460 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 | |
| 14 to 18 |
| Strength to Weight: Bending, points | 16 | |
| 15 to 18 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 14 |
| Thermal Shock Resistance, points | 11 | |
| 11 to 15 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.35 to 0.65 | |
| 0.13 to 0.16 |
| Chromium (Cr), % | 19 to 22 | |
| 0 |
| Cobalt (Co), % | 18.5 to 22 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 23 to 38.9 | |
| 98.4 to 99.269 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 2.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 18 to 22 | |
| 0 |
| Niobium (Nb), % | 0.75 to 1.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tungsten (W), % | 2.0 to 3.0 | |
| 0 |