EN 1.4874 Stainless Steel vs. C66700 Brass
EN 1.4874 stainless steel belongs to the iron alloys classification, while C66700 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4874 stainless steel and the bottom bar is C66700 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 6.7 | |
| 2.0 to 58 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 80 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 340 to 690 |
| Tensile Strength: Yield (Proof), MPa | 360 | |
| 100 to 640 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 1150 | |
| 140 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1090 |
| Melting Onset (Solidus), °C | 1400 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 13 | |
| 97 |
| Thermal Expansion, µm/m-K | 15 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 25 |
| Density, g/cm3 | 8.4 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 7.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 110 | |
| 45 |
| Embodied Water, L/kg | 290 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 13 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 | |
| 49 to 1900 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 16 | |
| 11 to 23 |
| Strength to Weight: Bending, points | 16 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 30 |
| Thermal Shock Resistance, points | 11 | |
| 11 to 23 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.65 | |
| 0 |
| Chromium (Cr), % | 19 to 22 | |
| 0 |
| Cobalt (Co), % | 18.5 to 22 | |
| 0 |
| Copper (Cu), % | 0 | |
| 68.5 to 71.5 |
| Iron (Fe), % | 23 to 38.9 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.8 to 1.5 |
| Molybdenum (Mo), % | 2.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 18 to 22 | |
| 0 |
| Niobium (Nb), % | 0.75 to 1.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 26.3 to 30.7 |
| Residuals, % | 0 | |
| 0 to 0.5 |