EN 1.4876 Stainless Steel vs. AWS ER110S-1

Both EN 1.4876 stainless steel and AWS ER110S-1 are iron alloys. They have 49% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4876 stainless steel and the bottom bar is AWS ER110S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 33
17
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 570
870
Tensile Strength: Yield (Proof), MPa 190
740

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
47
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 30
4.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.3
1.8
Embodied Energy, MJ/kg 76
25
Embodied Water, L/kg 200
55

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
140
Resilience: Unit (Modulus of Resilience), kJ/m3 94
1460
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
31
Strength to Weight: Bending, points 19
26
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 14
26

Alloy Composition

Aluminum (Al), % 0.15 to 0.6
0 to 0.1
Carbon (C), % 0 to 0.12
0 to 0.090
Chromium (Cr), % 19 to 23
0 to 0.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 38.6 to 50.7
92.8 to 96.3
Manganese (Mn), % 0 to 2.0
1.4 to 1.8
Molybdenum (Mo), % 0
0.25 to 0.55
Nickel (Ni), % 30 to 34
1.9 to 2.6
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 1.0
0.2 to 0.55
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0.15 to 0.6
0 to 0.1
Vanadium (V), % 0
0 to 0.040
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0
0 to 0.5