EN 1.4876 Stainless Steel vs. S35000 Stainless Steel

Both EN 1.4876 stainless steel and S35000 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4876 stainless steel and the bottom bar is S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 33
2.3 to 14
Fatigue Strength, MPa 150
380 to 520
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 370
740 to 950
Tensile Strength: Ultimate (UTS), MPa 570
1300 to 1570
Tensile Strength: Yield (Proof), MPa 190
660 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 490
410
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 14
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 30
14
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.3
3.2
Embodied Energy, MJ/kg 76
44
Embodied Water, L/kg 200
130

Common Calculations

PREN (Pitting Resistance) 21
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
28 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 94
1070 to 3360
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
46 to 56
Strength to Weight: Bending, points 19
34 to 38
Thermal Diffusivity, mm2/s 3.2
4.4
Thermal Shock Resistance, points 14
42 to 51

Alloy Composition

Aluminum (Al), % 0.15 to 0.6
0
Carbon (C), % 0 to 0.12
0.070 to 0.11
Chromium (Cr), % 19 to 23
16 to 17
Iron (Fe), % 38.6 to 50.7
72.7 to 76.9
Manganese (Mn), % 0 to 2.0
0.5 to 1.3
Molybdenum (Mo), % 0
2.5 to 3.2
Nickel (Ni), % 30 to 34
4.0 to 5.0
Nitrogen (N), % 0
0.070 to 0.13
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.15 to 0.6
0