EN 1.4877 Stainless Steel vs. ACI-ASTM CC50 Steel

Both EN 1.4877 stainless steel and ACI-ASTM CC50 steel are iron alloys. They have 69% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4877 stainless steel and the bottom bar is ACI-ASTM CC50 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
80
Tensile Strength: Ultimate (UTS), MPa 630
430

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 560
460
Maximum Temperature: Mechanical, °C 1150
1100
Melting Completion (Liquidus), °C 1400
1420
Melting Onset (Solidus), °C 1360
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 12
17
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 37
14
Density, g/cm3 8.0
7.6
Embodied Carbon, kg CO2/kg material 6.2
2.7
Embodied Energy, MJ/kg 89
39
Embodied Water, L/kg 220
170

Common Calculations

PREN (Pitting Resistance) 28
28
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 22
16
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 3.2
4.5
Thermal Shock Resistance, points 15
14

Alloy Composition

Aluminum (Al), % 0 to 0.025
0
Carbon (C), % 0.040 to 0.080
0 to 0.5
Cerium (Ce), % 0.050 to 0.1
0
Chromium (Cr), % 26 to 28
26 to 30
Iron (Fe), % 36.4 to 42.3
62.9 to 74
Manganese (Mn), % 0 to 1.0
0 to 1.0
Nickel (Ni), % 31 to 33
0 to 4.0
Niobium (Nb), % 0.6 to 1.0
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 1.5
Sulfur (S), % 0 to 0.010
0 to 0.040