EN 1.4886 Stainless Steel vs. AWS BVAg-30

EN 1.4886 stainless steel belongs to the iron alloys classification, while AWS BVAg-30 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is AWS BVAg-30.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
86
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 76
31
Tensile Strength: Ultimate (UTS), MPa 580
170

Thermal Properties

Latent Heat of Fusion, J/g 320
140
Melting Completion (Liquidus), °C 1390
810
Melting Onset (Solidus), °C 1340
810
Specific Heat Capacity, J/kg-K 480
280
Thermal Expansion, µm/m-K 15
19

Otherwise Unclassified Properties

Density, g/cm3 8.0
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.7
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 20
4.7
Strength to Weight: Bending, points 19
6.7
Thermal Shock Resistance, points 14
7.6

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.15
0 to 0.0050
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0
25.5 to 28.5
Iron (Fe), % 38.7 to 49
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0
Palladium (Pd), % 0
4.5 to 5.5
Phosphorus (P), % 0 to 0.030
0 to 0.0020
Silicon (Si), % 1.0 to 2.0
0
Silver (Ag), % 0
67 to 69
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 0.0010