EN 1.4886 Stainless Steel vs. S44800 Stainless Steel

Both EN 1.4886 stainless steel and S44800 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is S44800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 45
23
Fatigue Strength, MPa 280
300
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
82
Shear Strength, MPa 400
370
Tensile Strength: Ultimate (UTS), MPa 580
590
Tensile Strength: Yield (Proof), MPa 300
450

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Corrosion, °C 420
460
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
17
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
3.8
Embodied Energy, MJ/kg 76
52
Embodied Water, L/kg 190
190

Common Calculations

PREN (Pitting Resistance) 19
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
120
Resilience: Unit (Modulus of Resilience), kJ/m3 230
480
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 3.1
4.6
Thermal Shock Resistance, points 14
19

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.010
Chromium (Cr), % 17 to 20
28 to 30
Copper (Cu), % 0
0 to 0.15
Iron (Fe), % 38.7 to 49
62.6 to 66.5
Manganese (Mn), % 0 to 2.0
0 to 0.3
Molybdenum (Mo), % 0
3.5 to 4.2
Nickel (Ni), % 33 to 37
2.0 to 2.5
Nitrogen (N), % 0 to 0.1
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 1.0 to 2.0
0 to 0.2
Sulfur (S), % 0 to 0.015
0 to 0.020