EN 1.4887 Stainless Steel vs. Zamak 5

EN 1.4887 stainless steel belongs to the iron alloys classification, while Zamak 5 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4887 stainless steel and the bottom bar is Zamak 5.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
92
Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 45
6.3
Fatigue Strength, MPa 280
56
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 76
33
Shear Strength, MPa 400
260
Tensile Strength: Ultimate (UTS), MPa 580
330
Tensile Strength: Yield (Proof), MPa 300
240

Thermal Properties

Latent Heat of Fusion, J/g 320
120
Maximum Temperature: Mechanical, °C 1100
95
Melting Completion (Liquidus), °C 1390
390
Melting Onset (Solidus), °C 1350
380
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 12
110
Thermal Expansion, µm/m-K 15
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
26
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
37

Otherwise Unclassified Properties

Base Metal Price, % relative 39
12
Density, g/cm3 8.0
6.4
Embodied Carbon, kg CO2/kg material 6.7
3.0
Embodied Energy, MJ/kg 96
57
Embodied Water, L/kg 210
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
19
Resilience: Unit (Modulus of Resilience), kJ/m3 230
330
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 20
14
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 3.2
42
Thermal Shock Resistance, points 14
9.9

Alloy Composition

Aluminum (Al), % 0
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 20 to 23
0
Copper (Cu), % 0
0.7 to 1.3
Iron (Fe), % 34.2 to 45
0 to 0.1
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 0
0.025 to 0.080
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0 to 0.020
Niobium (Nb), % 1.0 to 1.5
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 1.0 to 2.0
0 to 0.030
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
94.3 to 95.7