EN 1.4889 Cast Nickel vs. EN 1.5510 Steel
EN 1.4889 cast nickel belongs to the nickel alloys classification, while EN 1.5510 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4889 cast nickel and the bottom bar is EN 1.5510 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 3.4 | |
| 11 to 21 |
| Fatigue Strength, MPa | 110 | |
| 220 to 330 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 450 to 1600 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 310 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1160 | |
| 400 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 120 | |
| 19 |
| Embodied Water, L/kg | 280 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 | |
| 46 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 260 to 710 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 16 to 57 |
| Strength to Weight: Bending, points | 18 | |
| 17 to 39 |
| Thermal Shock Resistance, points | 13 | |
| 13 to 47 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.35 to 0.45 | |
| 0.25 to 0.3 |
| Chromium (Cr), % | 32.5 to 37.5 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 10.5 to 21.2 | |
| 97.9 to 99.149 |
| Manganese (Mn), % | 1.0 to 1.5 | |
| 0.6 to 0.9 |
| Nickel (Ni), % | 42 to 46 | |
| 0 |
| Niobium (Nb), % | 1.5 to 2.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 1.5 to 2.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |