EN 1.4905 Stainless Steel vs. EN 1.0471 Steel

Both EN 1.4905 stainless steel and EN 1.0471 steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4905 stainless steel and the bottom bar is EN 1.0471 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
23
Fatigue Strength, MPa 330
270
Impact Strength: V-Notched Charpy, J 38
38
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 460
360
Tensile Strength: Ultimate (UTS), MPa 740
580
Tensile Strength: Yield (Proof), MPa 510
380

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 660
400
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1440
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
52
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 4.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.2
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 40
20
Embodied Water, L/kg 90
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 680
390
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26
20
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 7.0
14
Thermal Shock Resistance, points 25
18

Alloy Composition

Aluminum (Al), % 0 to 0.040
0 to 0.060
Boron (B), % 0.00050 to 0.0050
0
Carbon (C), % 0.090 to 0.13
0 to 0.22
Chromium (Cr), % 8.5 to 9.5
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 86.2 to 88.8
97.4 to 98.8
Manganese (Mn), % 0.3 to 0.6
1.0 to 1.5
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0.1 to 0.4
0
Niobium (Nb), % 0.060 to 0.1
0.015 to 0.1
Nitrogen (N), % 0.050 to 0.090
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.1 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.010
Tungsten (W), % 0.9 to 1.1
0
Vanadium (V), % 0.18 to 0.25
0