EN 1.4910 Stainless Steel vs. ASTM A369 Grade FP21

Both EN 1.4910 stainless steel and ASTM A369 grade FP21 are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4910 stainless steel and the bottom bar is ASTM A369 grade FP21.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 41
20
Fatigue Strength, MPa 250
160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Shear Strength, MPa 450
300
Tensile Strength: Ultimate (UTS), MPa 650
470
Tensile Strength: Yield (Proof), MPa 290
240

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 950
470
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1400
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
41
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 20
4.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.9
1.8
Embodied Energy, MJ/kg 54
23
Embodied Water, L/kg 150
61

Common Calculations

PREN (Pitting Resistance) 27
6.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
80
Resilience: Unit (Modulus of Resilience), kJ/m3 210
150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 4.3
11
Thermal Shock Resistance, points 14
14

Alloy Composition

Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0 to 0.040
0.050 to 0.15
Chromium (Cr), % 16 to 18
2.7 to 3.4
Iron (Fe), % 62 to 69.9
94.3 to 96.2
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 2.0 to 3.0
0.8 to 1.1
Nickel (Ni), % 12 to 14
0
Nitrogen (N), % 0.1 to 0.18
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.025