Both EN 1.4910 stainless steel and AWS E209 are iron alloys. They have 89% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.4910 stainless steel and the bottom bar is AWS E209.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 41
17
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
79
Tensile Strength: Ultimate (UTS), MPa 650
770

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 16
14

Otherwise Unclassified Properties

Base Metal Price, % relative 20
21
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.9
4.4
Embodied Energy, MJ/kg 54
63
Embodied Water, L/kg 150
180

Common Calculations

PREN (Pitting Resistance) 27
33
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
28
Strength to Weight: Bending, points 21
24
Thermal Shock Resistance, points 14
19

Alloy Composition

Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0 to 0.040
0 to 0.060
Chromium (Cr), % 16 to 18
20.5 to 24
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 62 to 69.9
51.5 to 64.3
Manganese (Mn), % 0 to 2.0
4.0 to 7.0
Molybdenum (Mo), % 2.0 to 3.0
1.5 to 3.0
Nickel (Ni), % 12 to 14
9.5 to 12
Nitrogen (N), % 0.1 to 0.18
0.1 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0
0.1 to 0.3