EN 1.4910 Stainless Steel vs. EN 1.4590 Stainless Steel

Both EN 1.4910 stainless steel and EN 1.4590 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4910 stainless steel and the bottom bar is EN 1.4590 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 41
26
Fatigue Strength, MPa 250
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 450
310
Tensile Strength: Ultimate (UTS), MPa 650
480
Tensile Strength: Yield (Proof), MPa 290
270

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 410
470
Maximum Temperature: Mechanical, °C 950
860
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
26
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
11
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 3.9
2.5
Embodied Energy, MJ/kg 54
37
Embodied Water, L/kg 150
120

Common Calculations

PREN (Pitting Resistance) 27
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.3
7.0
Thermal Shock Resistance, points 14
17

Alloy Composition

Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0 to 0.040
0 to 0.030
Chromium (Cr), % 16 to 18
16 to 17.5
Iron (Fe), % 62 to 69.9
79.7 to 83.7
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 12 to 14
0
Niobium (Nb), % 0
0.35 to 0.55
Nitrogen (N), % 0.1 to 0.18
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Zirconium (Zr), % 0
0 to 0.15