EN 1.4910 Stainless Steel vs. EN 1.4855 Stainless Steel

Both EN 1.4910 stainless steel and EN 1.4855 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4910 stainless steel and the bottom bar is EN 1.4855 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 41
4.6
Fatigue Strength, MPa 250
120
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 650
500
Tensile Strength: Yield (Proof), MPa 290
250

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Maximum Temperature: Corrosion, °C 410
610
Maximum Temperature: Mechanical, °C 950
1050
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
14
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 20
34
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.9
5.9
Embodied Energy, MJ/kg 54
85
Embodied Water, L/kg 150
200

Common Calculations

PREN (Pitting Resistance) 27
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
19
Resilience: Unit (Modulus of Resilience), kJ/m3 210
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.3
3.7
Thermal Shock Resistance, points 14
11

Alloy Composition

Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0 to 0.040
0.3 to 0.5
Chromium (Cr), % 16 to 18
23 to 25
Iron (Fe), % 62 to 69.9
42.6 to 51.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
0 to 0.5
Nickel (Ni), % 12 to 14
23 to 25
Niobium (Nb), % 0
0.8 to 1.8
Nitrogen (N), % 0.1 to 0.18
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.75
1.0 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.030