EN 1.4911 Stainless Steel vs. C41300 Brass
EN 1.4911 stainless steel belongs to the iron alloys classification, while C41300 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4911 stainless steel and the bottom bar is C41300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 11 | |
| 2.0 to 44 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 76 | |
| 42 |
| Shear Strength, MPa | 640 | |
| 230 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 1070 | |
| 300 to 630 |
| Tensile Strength: Yield (Proof), MPa | 970 | |
| 120 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 700 | |
| 180 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1040 |
| Melting Onset (Solidus), °C | 1410 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 20 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 20 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 49 | |
| 44 |
| Embodied Water, L/kg | 130 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2410 | |
| 69 to 1440 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 38 | |
| 9.6 to 20 |
| Strength to Weight: Bending, points | 30 | |
| 11 to 19 |
| Thermal Diffusivity, mm2/s | 5.4 | |
| 40 |
| Thermal Shock Resistance, points | 37 | |
| 11 to 22 |
Alloy Composition
| Boron (B), % | 0.0050 to 0.015 | |
| 0 |
| Carbon (C), % | 0.050 to 0.12 | |
| 0 |
| Chromium (Cr), % | 9.8 to 11.2 | |
| 0 |
| Cobalt (Co), % | 5.0 to 7.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 89 to 93 |
| Iron (Fe), % | 75.7 to 83.8 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0.3 to 1.3 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 1.0 | |
| 0 |
| Nickel (Ni), % | 0.2 to 1.2 | |
| 0 |
| Niobium (Nb), % | 0.2 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.035 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.1 to 0.8 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.7 to 1.3 |
| Tungsten (W), % | 0 to 0.7 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.4 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 5.1 to 10.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |