EN 1.4913 Stainless Steel vs. N08020 Stainless Steel
Both EN 1.4913 stainless steel and N08020 stainless steel are iron alloys. They have 50% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.4913 stainless steel and the bottom bar is N08020 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 14 to 22 | |
| 15 to 34 |
| Fatigue Strength, MPa | 320 to 480 | |
| 210 to 240 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Shear Strength, MPa | 550 to 590 | |
| 380 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 980 | |
| 610 to 620 |
| Tensile Strength: Yield (Proof), MPa | 480 to 850 | |
| 270 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 430 | |
| 490 |
| Maximum Temperature: Mechanical, °C | 700 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1410 |
| Melting Onset (Solidus), °C | 1410 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Conductivity, W/m-K | 24 | |
| 12 |
| Thermal Expansion, µm/m-K | 11 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 1.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 1.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 38 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 6.6 |
| Embodied Energy, MJ/kg | 41 | |
| 92 |
| Embodied Water, L/kg | 97 | |
| 220 |
Common Calculations
| PREN (Pitting Resistance) | 14 | |
| 28 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 160 | |
| 83 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 1860 | |
| 180 to 440 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 31 to 35 | |
| 21 |
| Strength to Weight: Bending, points | 26 to 28 | |
| 20 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 3.2 |
| Thermal Shock Resistance, points | 31 to 34 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.020 | |
| 0 |
| Boron (B), % | 0 to 0.0015 | |
| 0 |
| Carbon (C), % | 0.17 to 0.23 | |
| 0 to 0.070 |
| Chromium (Cr), % | 10 to 11.5 | |
| 19 to 21 |
| Copper (Cu), % | 0 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 84.5 to 88.3 | |
| 29.9 to 44 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 32 to 38 |
| Niobium (Nb), % | 0.25 to 0.55 | |
| 0 to 1.0 |
| Nitrogen (N), % | 0.050 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.035 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |