EN 1.4913 Stainless Steel vs. R30075 Cobalt
EN 1.4913 stainless steel belongs to the iron alloys classification, while R30075 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4913 stainless steel and the bottom bar is R30075 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 to 250 |
| Elongation at Break, % | 14 to 22 | |
| 12 |
| Fatigue Strength, MPa | 320 to 480 | |
| 250 to 840 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 82 to 98 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 980 | |
| 780 to 1280 |
| Tensile Strength: Yield (Proof), MPa | 480 to 850 | |
| 480 to 840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1360 |
| Melting Onset (Solidus), °C | 1410 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 24 | |
| 13 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 8.1 |
| Embodied Energy, MJ/kg | 41 | |
| 110 |
| Embodied Water, L/kg | 97 | |
| 530 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 160 | |
| 84 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 1860 | |
| 560 to 1410 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 to 17 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 31 to 35 | |
| 26 to 42 |
| Strength to Weight: Bending, points | 26 to 28 | |
| 22 to 31 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 3.5 |
| Thermal Shock Resistance, points | 31 to 34 | |
| 21 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.020 | |
| 0 to 0.1 |
| Boron (B), % | 0 to 0.0015 | |
| 0 to 0.010 |
| Carbon (C), % | 0.17 to 0.23 | |
| 0 to 0.35 |
| Chromium (Cr), % | 10 to 11.5 | |
| 27 to 30 |
| Cobalt (Co), % | 0 | |
| 58.7 to 68 |
| Iron (Fe), % | 84.5 to 88.3 | |
| 0 to 0.75 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 5.0 to 7.0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 0 to 0.5 |
| Niobium (Nb), % | 0.25 to 0.55 | |
| 0 |
| Nitrogen (N), % | 0.050 to 0.1 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Tungsten (W), % | 0 | |
| 0 to 0.2 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |