EN 1.4919 Stainless Steel vs. AISI 317L Stainless Steel

Both EN 1.4919 stainless steel and AISI 317L stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4919 stainless steel and the bottom bar is AISI 317L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
44
Fatigue Strength, MPa 200
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
82
Shear Strength, MPa 400
380
Tensile Strength: Ultimate (UTS), MPa 590
550
Tensile Strength: Yield (Proof), MPa 230
250

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 950
1010
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
14
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
21
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.8
4.3
Embodied Energy, MJ/kg 52
59
Embodied Water, L/kg 150
160

Common Calculations

PREN (Pitting Resistance) 26
31
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
200
Resilience: Unit (Modulus of Resilience), kJ/m3 130
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.3
3.8
Thermal Shock Resistance, points 13
12

Alloy Composition

Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0.040 to 0.080
0 to 0.030
Chromium (Cr), % 16.5 to 18.5
18 to 20
Iron (Fe), % 62.8 to 71.5
58 to 68
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 2.5
3.0 to 4.0
Nickel (Ni), % 10 to 13
11 to 15
Nitrogen (N), % 0 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030