EN 1.4919 Stainless Steel vs. AWS ERTi-5

EN 1.4919 stainless steel belongs to the iron alloys classification, while AWS ERTi-5 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4919 stainless steel and the bottom bar is AWS ERTi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 40
10
Fatigue Strength, MPa 200
470
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 78
40
Tensile Strength: Ultimate (UTS), MPa 590
900
Tensile Strength: Yield (Proof), MPa 230
830

Thermal Properties

Latent Heat of Fusion, J/g 290
410
Maximum Temperature: Mechanical, °C 950
340
Melting Completion (Liquidus), °C 1440
1610
Melting Onset (Solidus), °C 1400
1560
Specific Heat Capacity, J/kg-K 470
560
Thermal Conductivity, W/m-K 16
7.1
Thermal Expansion, µm/m-K 16
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
36
Density, g/cm3 7.9
4.4
Embodied Carbon, kg CO2/kg material 3.8
38
Embodied Energy, MJ/kg 52
610
Embodied Water, L/kg 150
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
87
Resilience: Unit (Modulus of Resilience), kJ/m3 130
3250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
35
Strength to Weight: Axial, points 21
56
Strength to Weight: Bending, points 20
46
Thermal Diffusivity, mm2/s 4.3
2.9
Thermal Shock Resistance, points 13
63

Alloy Composition

Aluminum (Al), % 0
5.5 to 6.8
Boron (B), % 0.0015 to 0.0050
0
Carbon (C), % 0.040 to 0.080
0 to 0.050
Chromium (Cr), % 16.5 to 18.5
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 62.8 to 71.5
0 to 0.22
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 10 to 13
0
Nitrogen (N), % 0 to 0.1
0 to 0.030
Oxygen (O), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
88.2 to 90.9
Vanadium (V), % 0
3.5 to 4.5