EN 1.4922 Stainless Steel vs. EN 1.4487 Stainless Steel

Both EN 1.4922 stainless steel and EN 1.4487 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4922 stainless steel and the bottom bar is EN 1.4487 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
34
Fatigue Strength, MPa 330
210
Impact Strength: V-Notched Charpy, J 38
90
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 770
560
Tensile Strength: Yield (Proof), MPa 550
260

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 380
420
Maximum Temperature: Mechanical, °C 720
960
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 24
16
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.8
3.1
Embodied Energy, MJ/kg 40
44
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 15
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
160
Resilience: Unit (Modulus of Resilience), kJ/m3 770
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
20
Strength to Weight: Bending, points 24
19
Thermal Diffusivity, mm2/s 6.5
4.2
Thermal Shock Resistance, points 27
16

Alloy Composition

Carbon (C), % 0.17 to 0.23
0 to 0.030
Chromium (Cr), % 10 to 12.5
18 to 20
Iron (Fe), % 83.5 to 88.2
64.7 to 72.9
Manganese (Mn), % 0.3 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.8 to 1.2
0
Nickel (Ni), % 0.3 to 0.8
9.0 to 12
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0.2 to 0.35
0