EN 1.4922 Stainless Steel vs. EN 1.8062 Steel

Both EN 1.4922 stainless steel and EN 1.8062 steel are iron alloys. They have 88% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4922 stainless steel and the bottom bar is EN 1.8062 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 770
660 to 1910

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 720
420
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 24
43
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
2.4
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 40
20
Embodied Water, L/kg 100
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
24 to 69
Strength to Weight: Bending, points 24
22 to 44
Thermal Diffusivity, mm2/s 6.5
12
Thermal Shock Resistance, points 27
20 to 57

Alloy Composition

Carbon (C), % 0.17 to 0.23
0.42 to 0.5
Chromium (Cr), % 10 to 12.5
0.5 to 0.8
Iron (Fe), % 83.5 to 88.2
95.9 to 97.1
Manganese (Mn), % 0.3 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 0.8 to 1.2
0.2 to 0.3
Nickel (Ni), % 0.3 to 0.8
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.4
1.3 to 1.7
Sulfur (S), % 0 to 0.015
0 to 0.025
Vanadium (V), % 0.2 to 0.35
0