EN 1.4923 Stainless Steel vs. ASTM A372 Grade F Steel
Both EN 1.4923 stainless steel and ASTM A372 grade F steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4923 stainless steel and the bottom bar is ASTM A372 grade F steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 12 to 21 | |
20 to 22 |
Fatigue Strength, MPa | 300 to 440 | |
310 to 380 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 76 | |
73 |
Shear Strength, MPa | 540 to 590 | |
410 to 570 |
Tensile Strength: Ultimate (UTS), MPa | 870 to 980 | |
650 to 910 |
Tensile Strength: Yield (Proof), MPa | 470 to 780 | |
430 to 550 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
250 |
Maximum Temperature: Mechanical, °C | 740 | |
420 |
Melting Completion (Liquidus), °C | 1450 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1420 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 24 | |
44 |
Thermal Expansion, µm/m-K | 11 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
7.3 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
8.4 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 8.0 | |
2.4 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 2.9 | |
1.5 |
Embodied Energy, MJ/kg | 41 | |
20 |
Embodied Water, L/kg | 100 | |
51 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 150 | |
130 to 160 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 1580 | |
500 to 810 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 31 to 35 | |
23 to 32 |
Strength to Weight: Bending, points | 26 to 28 | |
21 to 27 |
Thermal Diffusivity, mm2/s | 6.5 | |
12 |
Thermal Shock Resistance, points | 30 to 34 | |
19 to 27 |
Alloy Composition
Carbon (C), % | 0.18 to 0.24 | |
0.3 to 0.4 |
Chromium (Cr), % | 11 to 12.5 | |
0.8 to 1.2 |
Iron (Fe), % | 83.5 to 87.1 | |
96.8 to 97.9 |
Manganese (Mn), % | 0.4 to 0.9 | |
0.7 to 1.0 |
Molybdenum (Mo), % | 0.8 to 1.2 | |
0.15 to 0.25 |
Nickel (Ni), % | 0.3 to 0.8 | |
0 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.015 |
Silicon (Si), % | 0 to 0.5 | |
0.15 to 0.35 |
Sulfur (S), % | 0 to 0.015 | |
0 to 0.010 |
Vanadium (V), % | 0.25 to 0.35 | |
0 |