EN 1.4923 Stainless Steel vs. SAE-AISI 52100 Steel
Both EN 1.4923 stainless steel and SAE-AISI 52100 steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4923 stainless steel and the bottom bar is SAE-AISI 52100 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 21 | |
| 10 to 20 |
| Fatigue Strength, MPa | 300 to 440 | |
| 250 to 340 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 72 |
| Shear Strength, MPa | 540 to 590 | |
| 370 to 420 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 980 | |
| 590 to 2010 |
| Tensile Strength: Yield (Proof), MPa | 470 to 780 | |
| 360 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 430 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 24 | |
| 47 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 to 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.5 |
| Embodied Energy, MJ/kg | 41 | |
| 20 |
| Embodied Water, L/kg | 100 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 150 | |
| 54 to 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 1580 | |
| 350 to 840 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 31 to 35 | |
| 21 to 72 |
| Strength to Weight: Bending, points | 26 to 28 | |
| 20 to 45 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 13 |
| Thermal Shock Resistance, points | 30 to 34 | |
| 19 to 61 |
Alloy Composition
| Carbon (C), % | 0.18 to 0.24 | |
| 0.93 to 1.1 |
| Chromium (Cr), % | 11 to 12.5 | |
| 1.4 to 1.6 |
| Iron (Fe), % | 83.5 to 87.1 | |
| 96.5 to 97.3 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0.25 to 0.45 |
| Molybdenum (Mo), % | 0.8 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0.3 to 0.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Vanadium (V), % | 0.25 to 0.35 | |
| 0 |