EN 1.4923 Stainless Steel vs. ZA-27
EN 1.4923 stainless steel belongs to the iron alloys classification, while ZA-27 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.4923 stainless steel and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 78 |
| Elongation at Break, % | 12 to 21 | |
| 2.0 to 4.5 |
| Fatigue Strength, MPa | 300 to 440 | |
| 110 to 170 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 76 | |
| 31 |
| Shear Strength, MPa | 540 to 590 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 980 | |
| 400 to 430 |
| Tensile Strength: Yield (Proof), MPa | 470 to 780 | |
| 260 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 130 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 120 |
| Melting Completion (Liquidus), °C | 1450 | |
| 480 |
| Melting Onset (Solidus), °C | 1410 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 530 |
| Thermal Conductivity, W/m-K | 24 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 53 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 4.2 |
| Embodied Energy, MJ/kg | 41 | |
| 80 |
| Embodied Water, L/kg | 100 | |
| 570 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 150 | |
| 8.1 to 18 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 1580 | |
| 420 to 890 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 28 |
| Strength to Weight: Axial, points | 31 to 35 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 26 to 28 | |
| 24 to 25 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 47 |
| Thermal Shock Resistance, points | 30 to 34 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 25 to 28 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0.18 to 0.24 | |
| 0 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 2.0 to 2.5 |
| Iron (Fe), % | 83.5 to 87.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.010 to 0.020 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 0.8 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0.3 to 0.8 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.080 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Vanadium (V), % | 0.25 to 0.35 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 69.3 to 73 |