EN 1.4938 Stainless Steel vs. EN 1.7108 Steel
Both EN 1.4938 stainless steel and EN 1.7108 steel are iron alloys. They have 84% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is EN 1.7108 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1030 | |
| 670 to 2070 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 46 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 1.5 |
| Embodied Energy, MJ/kg | 47 | |
| 20 |
| Embodied Water, L/kg | 110 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 31 to 37 | |
| 24 to 75 |
| Strength to Weight: Bending, points | 26 to 29 | |
| 22 to 47 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 12 |
| Thermal Shock Resistance, points | 30 to 35 | |
| 20 to 63 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.15 | |
| 0.57 to 0.65 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0.2 to 0.45 |
| Iron (Fe), % | 80.5 to 84.8 | |
| 95.9 to 96.9 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 1.5 to 2.0 | |
| 0 |
| Nickel (Ni), % | 2.0 to 3.0 | |
| 0 |
| Nitrogen (N), % | 0.020 to 0.040 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 1.6 to 2.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.025 |
| Vanadium (V), % | 0.25 to 0.4 | |
| 0 |