EN 1.4938 Stainless Steel vs. R60706 Alloy
EN 1.4938 stainless steel belongs to the iron alloys classification, while R60706 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is R60706 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 98 |
| Elongation at Break, % | 16 to 17 | |
| 16 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1030 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 640 to 870 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 30 | |
| 17 |
| Thermal Expansion, µm/m-K | 11 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.7 |
| Embodied Water, L/kg | 110 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 82 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1050 to 1920 | |
| 760 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 31 to 37 | |
| 24 |
| Strength to Weight: Bending, points | 26 to 29 | |
| 23 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 9.5 |
| Thermal Shock Resistance, points | 30 to 35 | |
| 67 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.15 | |
| 0 to 0.050 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 to 0.2 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 80.5 to 84.8 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 1.5 to 2.0 | |
| 0 |
| Nickel (Ni), % | 2.0 to 3.0 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0.020 to 0.040 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Vanadium (V), % | 0.25 to 0.4 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 91 to 98 |