EN 1.4945 Stainless Steel vs. C48200 Brass
EN 1.4945 stainless steel belongs to the iron alloys classification, while C48200 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4945 stainless steel and the bottom bar is C48200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 19 to 34 | |
| 15 to 40 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Shear Strength, MPa | 430 to 460 | |
| 260 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 740 | |
| 400 to 500 |
| Tensile Strength: Yield (Proof), MPa | 290 to 550 | |
| 160 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 120 |
| Melting Completion (Liquidus), °C | 1490 | |
| 900 |
| Melting Onset (Solidus), °C | 1440 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 14 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 23 |
| Density, g/cm3 | 8.1 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 5.0 | |
| 2.7 |
| Embodied Energy, MJ/kg | 73 | |
| 47 |
| Embodied Water, L/kg | 150 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 180 | |
| 61 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 760 | |
| 120 to 500 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 15 to 17 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 38 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 13 to 16 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.1 | |
| 0 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 59 to 62 |
| Iron (Fe), % | 57.9 to 65.7 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0.4 to 1.0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 15.5 to 17.5 | |
| 0 |
| Niobium (Nb), % | 0.4 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0.060 to 0.14 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.0 |
| Tungsten (W), % | 2.5 to 3.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 35.5 to 40.1 |
| Residuals, % | 0 | |
| 0 to 0.4 |