EN 1.4948 Stainless Steel vs. S20433 Stainless Steel

Both EN 1.4948 stainless steel and S20433 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4948 stainless steel and the bottom bar is S20433 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 48
46
Fatigue Strength, MPa 200
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Shear Strength, MPa 430
440
Tensile Strength: Ultimate (UTS), MPa 610
630
Tensile Strength: Yield (Proof), MPa 210
270

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 930
900
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1380
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 15
13
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.7
Embodied Energy, MJ/kg 43
39
Embodied Water, L/kg 140
150

Common Calculations

PREN (Pitting Resistance) 19
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
230
Resilience: Unit (Modulus of Resilience), kJ/m3 110
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
23
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 4.5
4.0
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0.040 to 0.080
0 to 0.080
Chromium (Cr), % 17 to 19
17 to 18
Copper (Cu), % 0
1.5 to 3.5
Iron (Fe), % 66.8 to 75
64.1 to 72.4
Manganese (Mn), % 0 to 2.0
5.5 to 7.5
Nickel (Ni), % 8.0 to 11
3.5 to 5.5
Nitrogen (N), % 0 to 0.1
0.1 to 0.25
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030