EN 1.4958 Stainless Steel vs. ASTM A182 Grade F3V

Both EN 1.4958 stainless steel and ASTM A182 grade F3V are iron alloys. They have 49% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4958 stainless steel and the bottom bar is ASTM A182 grade F3V.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
20
Fatigue Strength, MPa 170
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Shear Strength, MPa 430
410
Tensile Strength: Ultimate (UTS), MPa 630
660
Tensile Strength: Yield (Proof), MPa 190
470

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1090
470
Melting Completion (Liquidus), °C 1400
1470
Melting Onset (Solidus), °C 1350
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
39
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 30
4.2
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.3
2.3
Embodied Energy, MJ/kg 75
33
Embodied Water, L/kg 200
63

Common Calculations

PREN (Pitting Resistance) 21
6.3
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
120
Resilience: Unit (Modulus of Resilience), kJ/m3 95
590
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
23
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 3.2
10
Thermal Shock Resistance, points 15
19

Alloy Composition

Aluminum (Al), % 0.2 to 0.5
0
Boron (B), % 0
0.0010 to 0.0030
Carbon (C), % 0.030 to 0.080
0.050 to 0.18
Chromium (Cr), % 19 to 22
2.8 to 3.2
Cobalt (Co), % 0 to 0.5
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 41.1 to 50.6
94.4 to 95.7
Manganese (Mn), % 0 to 1.5
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 30 to 32.5
0
Niobium (Nb), % 0 to 0.1
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0 to 0.7
0 to 0.1
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0.2 to 0.5
0.015 to 0.035
Vanadium (V), % 0
0.2 to 0.3