EN 1.4958 Stainless Steel vs. EN 1.0453 Steel

Both EN 1.4958 stainless steel and EN 1.0453 steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4958 stainless steel and the bottom bar is EN 1.0453 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
26
Fatigue Strength, MPa 170
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 430
320
Tensile Strength: Ultimate (UTS), MPa 630
490
Tensile Strength: Yield (Proof), MPa 190
300

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1090
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.1
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.3
1.5
Embodied Energy, MJ/kg 75
20
Embodied Water, L/kg 200
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 95
230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 15
15

Alloy Composition

Aluminum (Al), % 0.2 to 0.5
0.020 to 0.060
Carbon (C), % 0.030 to 0.080
0 to 0.2
Chromium (Cr), % 19 to 22
0 to 0.3
Cobalt (Co), % 0 to 0.5
0
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 41.1 to 50.6
96.9 to 99.38
Manganese (Mn), % 0 to 1.5
0.6 to 1.4
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 30 to 32.5
0 to 0.3
Niobium (Nb), % 0 to 0.1
0 to 0.010
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0.2 to 0.5
0 to 0.040
Vanadium (V), % 0
0 to 0.020