MakeItFrom.com
Menu (ESC)

EN 1.4961 Stainless Steel vs. AISI 440B Stainless Steel

Both EN 1.4961 stainless steel and AISI 440B stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4961 stainless steel and the bottom bar is AISI 440B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
3.0 to 18
Fatigue Strength, MPa 190
260 to 850
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 420
460 to 1110
Tensile Strength: Ultimate (UTS), MPa 610
740 to 1930
Tensile Strength: Yield (Proof), MPa 220
430 to 1860

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 510
390
Maximum Temperature: Mechanical, °C 890
870
Melting Completion (Liquidus), °C 1430
1480
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
23
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 21
9.0
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
2.2
Embodied Energy, MJ/kg 57
31
Embodied Water, L/kg 140
120

Common Calculations

PREN (Pitting Resistance) 16
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
57 to 110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
27 to 70
Strength to Weight: Bending, points 20
24 to 45
Thermal Diffusivity, mm2/s 4.3
6.1
Thermal Shock Resistance, points 14
27 to 70

Alloy Composition

Carbon (C), % 0.040 to 0.1
0.75 to 1.0
Chromium (Cr), % 15 to 17
16 to 18
Iron (Fe), % 65.6 to 72.3
78.2 to 83.3
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 12 to 14
0
Niobium (Nb), % 0.4 to 1.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.3 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015