EN 1.4962 Stainless Steel vs. Grade TDCrV Steel
Both EN 1.4962 stainless steel and grade TDCrV steel are iron alloys. They have 67% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4962 stainless steel and the bottom bar is grade TDCrV steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 210 | |
| 520 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 690 | |
| 1730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 410 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1450 |
| Melting Onset (Solidus), °C | 1440 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 14 | |
| 49 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 2.1 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 1.9 |
| Embodied Energy, MJ/kg | 59 | |
| 26 |
| Embodied Water, L/kg | 150 | |
| 49 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 61 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 41 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 13 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 51 |
Alloy Composition
| Boron (B), % | 0.0015 to 0.0060 | |
| 0 |
| Carbon (C), % | 0.070 to 0.15 | |
| 0.62 to 0.72 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 0.4 to 0.6 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 62.1 to 69 | |
| 97.8 to 98.8 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.5 to 0.9 |
| Nickel (Ni), % | 12.5 to 14.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.3 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0.4 to 0.7 | |
| 0 |
| Tungsten (W), % | 2.5 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |