EN 1.4962 Stainless Steel vs. C64200 Bronze
EN 1.4962 stainless steel belongs to the iron alloys classification, while C64200 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4962 stainless steel and the bottom bar is C64200 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 22 to 34 | |
| 14 to 35 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 42 |
| Shear Strength, MPa | 420 to 440 | |
| 330 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 690 | |
| 540 to 640 |
| Tensile Strength: Yield (Proof), MPa | 260 to 490 | |
| 230 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 210 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1000 |
| Melting Onset (Solidus), °C | 1440 | |
| 980 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 14 | |
| 45 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 29 |
| Density, g/cm3 | 8.1 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 3.0 |
| Embodied Energy, MJ/kg | 59 | |
| 50 |
| Embodied Water, L/kg | 150 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 170 | |
| 73 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 610 | |
| 240 to 470 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 13 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 20 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 6.3 to 7.6 |
| Arsenic (As), % | 0 | |
| 0 to 0.15 |
| Boron (B), % | 0.0015 to 0.0060 | |
| 0 |
| Carbon (C), % | 0.070 to 0.15 | |
| 0 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 88.2 to 92.2 |
| Iron (Fe), % | 62.1 to 69 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 12.5 to 14.5 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 1.5 to 2.2 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0.4 to 0.7 | |
| 0 |
| Tungsten (W), % | 2.5 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |