EN 1.4962 Stainless Steel vs. N06650 Nickel

EN 1.4962 stainless steel belongs to the iron alloys classification, while N06650 nickel belongs to the nickel alloys. They have 46% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4962 stainless steel and the bottom bar is N06650 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 22 to 34
50
Fatigue Strength, MPa 210 to 330
420
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
82
Shear Strength, MPa 420 to 440
640
Tensile Strength: Ultimate (UTS), MPa 630 to 690
900
Tensile Strength: Yield (Proof), MPa 260 to 490
460

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Mechanical, °C 910
980
Melting Completion (Liquidus), °C 1480
1500
Melting Onset (Solidus), °C 1440
1450
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 23
60
Density, g/cm3 8.1
8.6
Embodied Carbon, kg CO2/kg material 4.1
10
Embodied Energy, MJ/kg 59
140
Embodied Water, L/kg 150
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 170
380
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 610
490
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21 to 24
29
Strength to Weight: Bending, points 20 to 21
24
Thermal Shock Resistance, points 14 to 16
24

Alloy Composition

Aluminum (Al), % 0
0.050 to 0.5
Boron (B), % 0.0015 to 0.0060
0
Carbon (C), % 0.070 to 0.15
0 to 0.030
Chromium (Cr), % 15.5 to 17.5
19 to 21
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 62.1 to 69
12 to 16
Manganese (Mn), % 0 to 1.5
0 to 0.5
Molybdenum (Mo), % 0
9.5 to 12.5
Nickel (Ni), % 12.5 to 14.5
44.4 to 58.9
Niobium (Nb), % 0
0.050 to 0.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0.4 to 0.7
0
Tungsten (W), % 2.5 to 3.0
0.5 to 2.5