EN 1.4971 Stainless Steel vs. AISI W1 Steel
Both EN 1.4971 stainless steel and AISI W1 steel are iron alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.4971 stainless steel and the bottom bar is AISI W1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 800 | |
| 590 to 2320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 48 |
| Thermal Expansion, µm/m-K | 15 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 2.2 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.6 | |
| 1.6 |
| Embodied Energy, MJ/kg | 110 | |
| 21 |
| Embodied Water, L/kg | 300 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 21 to 83 |
| Strength to Weight: Bending, points | 23 | |
| 20 to 50 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 13 |
| Thermal Shock Resistance, points | 19 | |
| 22 to 85 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.16 | |
| 0.7 to 1.5 |
| Chromium (Cr), % | 20 to 22.5 | |
| 0 to 0.15 |
| Cobalt (Co), % | 18.5 to 21 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Iron (Fe), % | 24.3 to 37.1 | |
| 96.4 to 98.9 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.35 to 0.73 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 19 to 21 | |
| 0 to 0.2 |
| Niobium (Nb), % | 0.75 to 1.3 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.025 |
| Tungsten (W), % | 2.0 to 3.0 | |
| 0 to 0.15 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |