EN 1.4971 Stainless Steel vs. C11300 Copper
EN 1.4971 stainless steel belongs to the iron alloys classification, while C11300 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4971 stainless steel and the bottom bar is C11300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 120 |
| Elongation at Break, % | 34 | |
| 2.3 to 50 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 81 | |
| 43 |
| Shear Strength, MPa | 530 | |
| 160 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 800 | |
| 230 to 410 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 77 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1080 |
| Melting Onset (Solidus), °C | 1410 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 13 | |
| 390 |
| Thermal Expansion, µm/m-K | 15 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 32 |
| Density, g/cm3 | 8.4 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 7.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 110 | |
| 42 |
| Embodied Water, L/kg | 300 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 | |
| 8.5 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
| 25 to 690 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 26 | |
| 7.2 to 13 |
| Strength to Weight: Bending, points | 23 | |
| 9.4 to 14 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 110 |
| Thermal Shock Resistance, points | 19 | |
| 8.2 to 15 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.16 | |
| 0 |
| Chromium (Cr), % | 20 to 22.5 | |
| 0 |
| Cobalt (Co), % | 18.5 to 21 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.85 to 99.973 |
| Iron (Fe), % | 24.3 to 37.1 | |
| 0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 |
| Nickel (Ni), % | 19 to 21 | |
| 0 |
| Niobium (Nb), % | 0.75 to 1.3 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.050 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |