EN 1.4980 Stainless Steel vs. EN 1.3555 Steel
Both EN 1.4980 stainless steel and EN 1.3555 steel are iron alloys. They have 63% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.4980 stainless steel and the bottom bar is EN 1.3555 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 540 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1500 |
| Melting Onset (Solidus), °C | 1380 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 9.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 5.6 |
| Embodied Energy, MJ/kg | 87 | |
| 81 |
| Embodied Water, L/kg | 170 | |
| 90 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 18 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 36 | |
| 27 |
| Strength to Weight: Bending, points | 28 | |
| 23 |
| Thermal Shock Resistance, points | 22 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0.030 to 0.080 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 13.5 to 16 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 49.2 to 58.5 | |
| 85.4 to 87.7 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.15 to 0.35 |
| Molybdenum (Mo), % | 1.0 to 1.5 | |
| 4.0 to 4.5 |
| Nickel (Ni), % | 24 to 27 | |
| 3.2 to 3.6 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.1 to 0.25 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 1.9 to 2.3 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0 to 0.15 |
| Vanadium (V), % | 0.1 to 0.5 | |
| 1.0 to 1.3 |