EN 1.4980 Stainless Steel vs. EN 1.8509 Steel
Both EN 1.4980 stainless steel and EN 1.8509 steel are iron alloys. They have 57% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.4980 stainless steel and the bottom bar is EN 1.8509 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 | |
| 11 |
| Fatigue Strength, MPa | 410 | |
| 580 |
| Impact Strength: V-Notched Charpy, J | 57 | |
| 29 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Shear Strength, MPa | 630 | |
| 680 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 | |
| 1130 |
| Tensile Strength: Yield (Proof), MPa | 680 | |
| 940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 440 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1450 |
| Melting Onset (Solidus), °C | 1380 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 39 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 2.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 1.6 |
| Embodied Energy, MJ/kg | 87 | |
| 22 |
| Embodied Water, L/kg | 170 | |
| 65 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 2.6 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1180 | |
| 2340 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 36 | |
| 40 |
| Strength to Weight: Bending, points | 28 | |
| 31 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 10 |
| Thermal Shock Resistance, points | 22 | |
| 33 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0.8 to 1.2 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0.030 to 0.080 | |
| 0.38 to 0.45 |
| Chromium (Cr), % | 13.5 to 16 | |
| 1.5 to 1.8 |
| Iron (Fe), % | 49.2 to 58.5 | |
| 95.5 to 97.1 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 1.0 to 1.5 | |
| 0.2 to 0.35 |
| Nickel (Ni), % | 24 to 27 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.035 |
| Titanium (Ti), % | 1.9 to 2.3 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.5 | |
| 0 |