EN 1.4981 Stainless Steel vs. EN 1.0501 Steel

Both EN 1.4981 stainless steel and EN 1.0501 steel are iron alloys. They have 65% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4981 stainless steel and the bottom bar is EN 1.0501 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
19
Fatigue Strength, MPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 420
350
Tensile Strength: Ultimate (UTS), MPa 610
560
Tensile Strength: Yield (Proof), MPa 240
280

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
48
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.4
Embodied Energy, MJ/kg 67
19
Embodied Water, L/kg 150
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
90
Resilience: Unit (Modulus of Resilience), kJ/m3 150
210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.3
13
Thermal Shock Resistance, points 14
18

Alloy Composition

Carbon (C), % 0.040 to 0.1
0.32 to 0.39
Chromium (Cr), % 15.5 to 17.5
0 to 0.4
Iron (Fe), % 59.6 to 66.7
97.4 to 99.18
Manganese (Mn), % 0 to 1.5
0.5 to 0.8
Molybdenum (Mo), % 1.6 to 2.0
0 to 0.1
Nickel (Ni), % 15.5 to 17.5
0 to 0.4
Niobium (Nb), % 0.4 to 1.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.3 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.045